Low Alloy Tool Steel Plate, Material #1.1620
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-08-31 20:01
- Browse the number:
152
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.huaxinfrp.com/
Product details
Model Number: ZXL056
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
Descriptions:Low alloyed carbon tool steel with good harden abilityApplications:Forging hammers and tools, punchers for paper and skin, agricultural tools, tools for soft and medium hard rocksChemical composition (in weight%):C: 0.70
Si: 0.20
Mn: 0.25
Physical properties (average values) at ambient temperature:
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing:
Heat to 680-720°C, cool slowly in furnace
Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to approx 600-650°C, holding for 1-2 hours at heat, followed by air cooling
Operation is performed to reduce distortion during heat treatment
Hardening
Harden from a temperature of 790-820°C followed by water quenching, hardness after quenching is 63 HRC
Forging
Hot forming temperature: 1050-800°C
Specifications:
Grade:mat number 1.1620
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’srequirements
Delivery: 7-20 days after received deposit of T/T
Si: 0.20
Mn: 0.25
Physical properties (average values) at ambient temperature:
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing:
Heat to 680-720°C, cool slowly in furnace
Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to approx 600-650°C, holding for 1-2 hours at heat, followed by air cooling
Operation is performed to reduce distortion during heat treatment
Hardening
Harden from a temperature of 790-820°C followed by water quenching, hardness after quenching is 63 HRC
Forging
Hot forming temperature: 1050-800°C
Specifications:
Grade:mat number 1.1620
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’srequirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Neoprene Faced Phenolic Gasket
price: Negotiable
-
Float Laminated Glass
price: Negotiable
-
Potato Planter Machine
price: Negotiable
-
Glass Food Container with Full Compartment
price: Negotiable
-
Corrugated Roof Sheet Making Machine
price: Negotiable
-
2 LED Forklift Blue Light
price: Negotiable