Low alloy tool steel bar
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-12-09 06:43
- Browse the number:
176
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.huaxinfrp.com/
Product details
Model Number: ZXL029
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steelApplicationFor tough and wear resistant cutting tools (dies, punchers) for plate, woodworking toolsChemical composition (in weight %)C: 0.80
Si: 0.50
Mn: 0.40
Cr: 1.10
V: 0.30
W: 1.95
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.94
Soft annealing
Heat to 720-750℃, cool slowly in furnace
This will produce a maximum Brinell hardness of 250
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650℃, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden froma temperature of 860 to 900℃, followed by oil quenching. Hardness after quenching is min 62 HRC
Tempering
Tempering temperature: 150 to 400℃
Forging
Hot forming temperature: 1050 to 850℃
Specifications:
Grade: material number 1.2552
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer's requirements
Delivery lead-time: 7-20 days after received deposit of T/T
Si: 0.50
Mn: 0.40
Cr: 1.10
V: 0.30
W: 1.95
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.94
Soft annealing
Heat to 720-750℃, cool slowly in furnace
This will produce a maximum Brinell hardness of 250
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650℃, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden froma temperature of 860 to 900℃, followed by oil quenching. Hardness after quenching is min 62 HRC
Tempering
Tempering temperature: 150 to 400℃
Forging
Hot forming temperature: 1050 to 850℃
Specifications:
Grade: material number 1.2552
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer's requirements
Delivery lead-time: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
- Dimensions per Unit: 2 × 0.5 × 0.5 Meters
- Weight per Unit: 20 Kilograms
- Units per Export Carton: 5
- Export Carton Dimensions L/W/H: 2 × 0.5 × 0.5 Meters
- Export Carton Weight: 5 Tons (US)
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Neoprene Faced Phenolic Gasket
price: Negotiable
-
Float Laminated Glass
price: Negotiable
-
Potato Planter Machine
price: Negotiable
-
Glass Food Container with Full Compartment
price: Negotiable
-
Corrugated Roof Sheet Making Machine
price: Negotiable
-
2 LED Forklift Blue Light
price: Negotiable